Опис Инцонел 600

---

Инцонел600 је рано развијена легура за јачање чврстог раствора на бази никла-хрома и гвожђа, која има добру отпорност на корозију и оксидацију на високим температурама, одличне перформансе процеса топлог и хладног прераде и заваривања, и има задовољавајућу топлотну чврстоћу и високу пластичност.

The alloy can be strengthened by cold working, and can also be connected by resistance welding, solution welding or brazing. It can supply cold-rolled thin plate, hot-rolled thick plate, strip, wire, bar, round cake, ring blank, ring ковање, etc. It is suitable for making anti-oxidation parts with low load below 1100 ℃. Alloy 600 is a non-magnetic nickel-based superalloy that combines high strength, hot and cold workability and corrosion resistance. And the alloy exhibits very good heat resistance. During the entire annealing to severe cold working process, there will be no aging corrosion or stress corrosion.

---

Inconel 600 chemical composition

Carbon 0.10% or less

Sulfur 0.015% or less

Chrome 14.00-17.00%

Бакар 0.50%

Manganese below 1.00%

Silicon 0.50% or less

Nickel 72.00% or more

Iron 6.00-10.00%

---

Inconel 600 Physical Properties

Specific gravity: 8.43

Густина: 0.3070 лб / ин3

Average specific heat (77-212 ° F): 0.1090 Btu / lb / ° F

Просечни коефицијент топлотног ширења

 

Thermal conductivity: 104.0BTU-in / hr / ft2 / ° F

Модул еластичности (Е)

Tension and compression: 31.0 X 103 ksi

Torsion and compression: 11.0 X 103 ksi

Отпор (77 ° Ф): 620.0 охм-цир-мил / фт

Melting distance: 2540 ° F

---

Effect of cold rolling on hardness

---

Inconel 600 Stress cracking strength

---

Tensile strength of warming environment

---

Механичко понашање

---

heat треатмент

Alloy 600 can not be hardened with age, but can be hardened by cold work.

The temperature at which the softening annealing starts is 871 ° C, and the annealing can be finished by heating at 982 ° C for 10-15 minutes. Exceeding 982 ° C will produce undesirable grain growth, but a little heating at 1038 ° C can completely soften the material without excessive grain growth.

The cooling rate does not affect the softening effect, so it can be quenched with water or air cooled.

---

Термичка обрада

Low sulfur reduction furnace atmosphere can be used to forge 600 alloy. Most of the work of thermal machining should be carried out in the temperature range of 1260-1010 ° C, a small amount of thermal machining can continue until the temperature drops to 871 ° C. The ductility of the material is low between 871 and 649 ° C, so it is not suitable for hot processing.

---

Inconel 600 Machine Plus

Both the hot-worked state and the annealed state of alloy 600 can be machined. Because this material generates a lot of heat when machined, high-speed steel, non-ferrous metal castings or cemented carbide tools should be used, and the tools should be kept sharp.

The turning speed of high-speed steel and non-ferrous metal tools is 0.18-0.23m / s, and the turning speed of cemented carbide tools is 0.51-0.89m / s. The speed range is an average value, and the speed and feed amount need to be adjusted according to the actual situation of the workpiece.

Lubricants need to be sulfur based. Before heating, such as welding, the lubricant must be completely removed.

Линк до овог чланка: Шта је Инцонел 600?

Изјава о поновном штампању: Ако нема посебних упутстава, сви чланци на овој страници су оригинални. Наведите извор за поновно штампање: хттпс: //ввв.цнцмацхинингптј.цом/，хвала！

---

ПТЈ ЦНЦ продавница производи делове са одличним механичким својствима, тачношћу и поновљивошћу од метала и пластике. Доступно 5-осно ЦНЦ глодање.Обрада високотемпературне легуре опсег инклудирање обрада инконела,обрада монелом,Машинска обрада геек аскологије,Шаран 49 обрада,Хастеллои обрада,Машинска обрада Нитрониц-60,Машинска обрада Химу 80,Алатна обрада челика, итд.,. Идеално за свемирске примене.ЦНЦ обрада производи делове са одличним механичким својствима, тачношћу и поновљивошћу од метала и пластике. Доступно ЦНЦ глодање са 3 и 5 осовина. Ми ћемо заједно са вама стратешки понудити најисплативије услуге које ће вам помоћи да постигнете свој циљ, добродошли да нас контактирате ( салес@пинтејин.цом ) директно за ваш нови пројекат.